德國朗盛 PA6 Durethan B 30 S F30 產品特性：B30S，5VA阻燃

我公司提供的產品均為正牌塑膠原料，品質保證，貨源穩定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權威資料請致電13268582149

PA6 B30S 物性表：

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183
Molding Shrinkage			ISO 294-4
Across Flow: 260°C, 2.00 mm 2	0.90	%
Across Flow: 120°C, 4 hr, 2.00 mm 3	0.30	%
Flow: 260°C, 2.00 mm 2	0.90	%
Flow: 120°C, 4 hr, 2.00 mm 3	0.30	%
Residual Moisture Content 4	0.030 to 0.070	%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3500	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	80.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	3.8	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	9.0	%	ISO 527-2/50
Flexural Modulus 5 (23°C)	3300	MPa	ISO 178/A
Flexural Strength 5			ISO 178/A
3.5% Strain, 23°C	105	MPa
23°C	120	MPa
Flexural Strain at Flexural Strength 6 (23°C)	5.5	%	ISO 178/A
Impact	Nominal Value	Unit	Test Method
Unnotched Izod Impact Strength (23°C)	100	kJ/m²	ISO 180/1U
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	65.0	°C	ISO 75-2/A
Ball Pressure Test (207°C)	Pass		IEC 60695-10-2
Melting Temperature 7	222	°C	ISO 11357-3
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+16	ohm	IEC 60093
Volume Resistivity (23°C)	1.0E+15	ohm·cm	IEC 60093
Electric Strength (23°C, 1.00 mm)	31	kV/mm	IEC 60243-1
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.380 mm	V-0
0.750 mm	V-0
1.50 mm	V-0
3.00 mm	V-0

PA6日本三菱工程1010C2 通用注塑級 剛性改良
PA6日本三菱工程1010N2 通用注塑級 剛性改良、脫模性改良
PA6日本三菱工程1010N2-1ES 通用注塑級
PA6日本三菱工程1010N2-2 通用注塑級
PA6日本三菱工程1011CH5 通用注塑級 剛性改良
PA6日本三菱工程1013C5 通用注塑級 流的性改良
PA6日本三菱工程1013G10-1 通用注塑級
PA6日本三菱工程1013G15-1 通用注塑級
PA6日本三菱工程1013G20-1 通用注塑級
PA6日本三菱工程1013G30-1 通用注塑級
PA6日本三菱工程1013G45-1 通用注塑級
PA6日本三菱工程1015F2 通用注塑級 剛性改良、流動性改良、涂裝性改良
PA6日本三菱工程1015G33 通用注塑級
PA6日本三菱工程1015G35 通用注塑級
PA6日本三菱工程1015GN2-30 通用注塑級
PA6日本三菱工程1015GSTH 通用注塑級
PA6日本三菱工程1020A7` 薄膜級 流的性改良、薄膜用
PA6日本三菱工程1022C6 通用注塑級 高粘度
PA6日本三菱工程1035GTX30 通用注塑級