基礎創新PC LEXAN ML6411 產品特性:無溴無鹵5VA級防火阻燃(2mm 能達到5VB),良好的流動性,良好的抗沖擊性,中等耐熱性,具備光屏蔽能力
我公司提供的產品均為正牌塑膠原料,品質保證,貨源穩定,送貨上門,可免費提供官方物性表、UL黃卡,并隨貨提供RoHS報告、SGS報告等,索取權威資料請致電13268582149
PC ML6411 物性表:
Physical |
Nominal Value |
Unit |
Test Method |
Specific Gravity |
1.19 |
g/cm³ |
ASTM D792 |
Density |
1.20 |
g/cm³ |
ISO 1183 |
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) |
7.0 |
g/10 min |
ASTM D1238 |
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) |
18.0 |
cm³/10min |
ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) |
0.40 to 0.80 |
% |
Internal Method |
Water Absorption (Saturation, 23°C) |
0.30 |
% |
ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) |
0.10 |
% |
ISO 62 |
Mechanical |
Nominal Value |
Unit |
Test Method |
Tensile Modulus 2 |
2500 |
MPa |
ASTM D638 |
Tensile Modulus |
2350 |
MPa |
ISO 527-2/1 |
Tensile Strength 3 (Yield) |
62.0 |
MPa |
ASTM D638 |
Tensile Stress (Yield) |
62.0 |
MPa |
ISO 527-2/50 |
Tensile Strength 3 (Break) |
54.0 |
MPa |
ASTM D638 |
Tensile Stress (Break) |
58.0 |
MPa |
ISO 527-2/50 |
Tensile Elongation 3 (Yield) |
5.0 |
% |
ASTM D638 |
Tensile Strain (Yield) |
5.0 |
% |
ISO 527-2/50 |
Tensile Elongation 3 (Break) |
100 |
% |
ASTM D638 |
Tensile Strain (Break) |
100 |
% |
ISO 527-2/50 |
Flexural Modulus 4 (50.0 mm Span) |
2600 |
MPa |
ASTM D790 |
Flexural Modulus 5 |
2350 |
MPa |
ISO 178 |
Flexural Strength 5, 6 |
90.0 |
MPa |
ISO 178 |
Flexural Strength 4 (Yield, 50.0 mm Span) |
95.0 |
MPa |
ASTM D790 |
Impact |
Nominal Value |
Unit |
Test Method |
Notched Izod Impact |
|
|
ASTM D256 |
-30°C |
150 |
J/m |
|
23°C |
900 |
J/m |
|
Notched Izod Impact Strength 7 |
|
|
ISO 180/1A |
-30°C |
15 |
kJ/m² |
|
23°C |
60 |
kJ/m² |
|
Instrumented Dart Impact (23°C, Total Energy) |
72.0 |
J |
ASTM D3763 |
Thermal |
Nominal Value |
Unit |
Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) |
128 |
°C |
ASTM D648 |
Heat Deflection Temperature 8 (0.45 MPa, Unannealed, 100 mm Span) |
125 |
°C |
ISO 75-2/Be |
Deflection Temperature Under Load |
|
|
ASTM D648 |
1.8 MPa, Unannealed, 3.20 mm |
114 |
°C |
|
1.8 MPa, Unannealed, 6.40 mm |
119 |
°C |
|
Heat Deflection Temperature 8 (1.8 MPa, Unannealed, 100 mm Span) |
115 |
°C |
ISO 75-2/Ae |
Vicat Softening Temperature |
134 |
°C |
ASTM D1525 9 |
Vicat Softening Temperature |
|
|
|
-- |
134 |
°C |
ISO 306/B50 |
-- |
135 |
°C |
ISO 306/B120 |
Ball Pressure Test (125°C) |
Pass |
|
IEC 60695-10-2 |
CLTE - Flow (-40 to 40°C) |
0.000077 |
cm/cm/°C |
ASTM E831 |
CLTE - Flow (-40 to 40°C) |
0.000070 |
cm/cm/°C |
ISO 11359-2 |
CLTE - Transverse (-40 to 40°C) |
0.000059 |
cm/cm/°C |
ASTM E831 |
CLTE - Transverse (-40 to 40°C) |
0.000070 |
cm/cm/°C |
ISO 11359-2 |
Electrical |
Nominal Value |
Unit |
Test Method |
Volume Resistivity |
> 1.0E+15 |
ohm·cm |
IEC 60093 |
Dielectric Strength (3.20 mm, in Oil) |
27 |
kV/mm |
ASTM D149 |
Comparative Tracking Index |
250 |
V |
IEC 60112 |
Flammability |
Nominal Value |
Unit |
Test Method |
Flame Rating - UL |
|
|
UL 94 |
1.50 mm |
V-0 |
|
|
3.00 mm |
5VA |
|
|
PC 基礎創新塑料(美國) 101 通用注塑級
PC 基礎創新塑料(美國) 101R 通用注塑級本色 加脫模劑,無鹵
PC 基礎創新塑料(美國) 103R-111 通用注塑級本色 添加脫模劑、紫外線穩定劑、無鹵。
PC 基礎創新塑料(美國) 121R 通用注塑級本色 加脫模劑,無鹵
PC 基礎創新塑料(美國) 131 通用注塑級本色 無鹵
PC 基礎創新塑料(美國) 131R-111 通用注塑級 一般級,超高粘度
PC 基礎創新塑料(美國) 141R 通用注塑級本色 加脫模劑,無鹵
PC 基礎創新塑料(美國) 141R-111 通用注塑級 一般級,UL 94HB,一般射出成形用,低粘度
PC 基礎創新塑料(美國) 141R-701 通用注塑級 通用級,UL 94HB,一般射出成形用,低粘底
PC 基礎創新塑料(美國) 143 通用注塑級本色 加紫外線穩定劑,無鹵
PC 基礎創新塑料(美國) 143R 通用注塑級本色 加脫模劑,紫外線穩定劑,無鹵
PC 基礎創新塑料(美國) 144R 通用注塑級本色 加脫模劑。
PC 基礎創新塑料(美國) 163 通用注塑級本色 加脫模劑、紫外線穩定劑,良好的可加工性,中等粘度
PC 基礎創新塑料(美國) 2034E 通用注塑級