杜邦POM Delrin 100 特性及用途：抗疲勞 良好的抗蠕變性、尺寸穩(wěn)定性以及韌性 高耐沖擊性 超高分子量 高剛度 高強(qiáng)度 高粘度 可超聲波焊接
主要用途：輸送機(jī) 工程機(jī)械配件 緊固件 齒輪 外殼 片材 管道
我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權(quán)威資料請致電13268582149
POM 100 物性表：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 1.0 | g/10 min | ASTM D1238 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.90 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (24 hr, 3.20 mm) | 1.8 to 2.1 | % | ASTM D955 |
| Molding Shrinkage - Across Flow (24 hr, 3.20 mm) | 1.8 to 2.1 | % | ASTM D955 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow: 2.00 mm | 1.9 | % | |
| Flow: 2.00 mm | 2.1 | % | |
| Water Absorption (23°C, 24 hr) | 0.27 | % | ASTM D570 |
| Water Absorption (Saturation, 23°C) | 0.90 | % | ASTM D570 |
| Water Absorption (Saturation, 23°C) | 0.90 | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.22 | % | ASTM D570 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 3 (23°C) | 3120 | MPa | ASTM D638 |
| Tensile Modulus (23°C) | 3100 | MPa | ISO 527-2 |
| Tensile Strength 3 | ASTM D638 | ||
| 70°C | 48.0 | MPa | |
| 100°C | 36.0 | MPa | |
| Tensile Strength 3 (Yield, 23°C) | 69.0 | MPa | ASTM D638 |
| Tensile Stress (Yield, 23°C) | 71.0 | MPa | ISO 527-2 |
| Tensile Elongation 3 (Yield, 23°C) | 25 | % | ASTM D638 |
| Tensile Strain (Yield, 23°C) | 25 | % | ISO 527-2 |
| Tensile Elongation 3 | ASTM D638 | ||
| Break, 23°C | 75 | % | |
| Break, 70°C | 230 | % | |
| Break, 100°C | > 250 | % | |
| Tensile Strain (Break, 23°C) | 70 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 45 | % | ISO 527-2 |
| Tensile Creep Modulus (1 hr) | 2900 | MPa | ISO 899-1 |
| Tensile Creep Modulus (1000 hr) | 1600 | MPa | ISO 899-1 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 2890 | MPa | |
| 70°C | 1550 | MPa | |
| 100°C | 900 | MPa | |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Flexural Strength (5.0% Strain, 23°C) | 99.0 | MPa | ASTM D790 |
| Flexural Strength (3.5% Strain, 23°C) | 76.0 | MPa | ISO 178 |
| Shear Strength (23°C) | 66.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 96 | J/m | |
| 23°C | 120 | J/m | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 13 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Tensile Impact Strength 4 (23°C) | 358 | kJ/m² | ASTM D1822 |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 94 | ||
| R-Scale | 120 |
POM 美國杜邦 100P-BK602 通用注塑級 高粘度，韌性，加工熱穩(wěn)定性
POM 美國杜邦 100P-NC010 通用注塑級 高粘度,韌性,加工熱穩(wěn)定性
POM 美國杜邦 100PE-NC010 通用注塑級 高粘度,注射成型,加工熱穩(wěn)定性
POM 美國杜邦 100ST-NC010 通用注塑級 超強(qiáng)硬,粘度高,抗沖擊性能,韌性
POM 美國杜邦 127UV-NC010 通用注塑級 高粘度，沖擊強(qiáng)度，紫外和熱穩(wěn)定性，汽車內(nèi)部應(yīng)用
POM 美國杜邦 150 通用注塑級 高粘度擠出，熱穩(wěn)定性，低模具沉淀，提高低孔隙度結(jié)晶。
POM 美國杜邦 23P 通用注塑級 均聚甲醛
POM 美國杜邦 390PM 通用注塑級
POM 美國杜邦 500AF 通用注塑級 中粘度，20%PTFE，低磨損
POM 美國杜邦 500CL-BK601 通用注塑級 中粘度，潤滑，低磨損
POM 美國杜邦 500CL-NC010 通用注塑級 中粘度,潤滑,低磨損
POM 美國杜邦 500P 通用注塑級本色 一般機(jī)械零件、齒輪、拉煉、凸輪。有素材可供機(jī)械加工。
POM 美國杜邦 500P-BK602 通用注塑級 中粘度，注塑成型，加工熱穩(wěn)定性
POM 美國杜邦 500P-NC010 通用注塑級本色 中粘度，注塑成型，加工熱穩(wěn)定性
POM 美國杜邦 500T-NC010 通用注塑級 中粘度,增韌,耐沖擊
POM 美國杜邦 511P 通用注塑級