東莞旺特公司低價供應無鹵阻燃增強PC 500ECR 無溴無氯 聚碳酸酯塑料

沙伯基礎創新PC LEXAN 500ECR 產品特性：含10%玻璃纖維增強，無溴無氯，防火阻燃（2.3mm），良好的剛度

PC 500ECR 物性表：

Specific Gravity	1.27	g/cm³	ASTM D792
Density	1.25	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	7.5	g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	7	cm³/10min	ISO 1133
Molding Shrinkage - Flow (3.20 mm)	0.40 to 0.60	%	Internal Method
Molding Shrinkage - Across Flow (3.20 mm)	0.40 to 0.60	%	Internal Method
Water Absorption (Saturation, 23°C)	0.31	%	ISO 62
Water Absorption (Equilibrium, 23°C, 50% RH)	0.13	%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus 2	2460	MPa	ASTM D638
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Strength 3 (Yield)	57	MPa	ASTM D638
Tensile Stress (Yield)	60	MPa	ISO 527-2/5
Tensile Strength 3 (Break)	48	MPa	ASTM D638
Tensile Stress (Break)	45	MPa	ISO 527-2/5
Tensile Elongation 3 (Yield)	4.7	%	ASTM D638
Tensile Strain (Yield)	5	%	ISO 527-2/5
Tensile Elongation 3 (Break)	46	%	ASTM D638
Tensile Strain (Break)	7	%	ISO 527-2/5
Flexural Modulus 4 (50.0 mm Span)	3120	MPa	ASTM D790
Flexural Modulus 5	3400	MPa	ISO 178
Flexural Strength 5, 6	95	MPa	ISO 178
Flexural Strength 4 (Break, 50.0 mm Span)	94	MPa	ASTM D790
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)	11	mg	Internal Method
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength
-30°C 7	9	kJ/m²	ISO 179/1eA
23°C 7	10	kJ/m²	ISO 179/1eA
23°C 8	9	kJ/m²	ISO 179/1eA
23°C	15	kJ/m²	ISO 179/2C
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C 8	No Break
-30°C 7	No Break
23°C 7	No Break
23°C 8	No Break
Notched Izod Impact			ASTM D256
-30°C	100	J/m
23°C	130	J/m
Notched Izod Impact Strength 9			ISO 180/1A
-30°C	8	kJ/m²
23°C	10	kJ/m²
Unnotched Izod Impact (23°C, 6.40 mm)	No Break		ASTM D4812
Unnotched Izod Impact Strength			ISO 180/1U
-30°C 10	No Break
-30°C 9	130	kJ/m²
23°C 9	No Break
23°C 10	No Break
Instrumented Dart Impact (23°C, Total Energy)	61	J	ASTM D3763
Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 358/30)	115	MPa	ISO 2039-1
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm)	143	°C	ASTM D648
Heat Deflection Temperature 11 (0.45 MPa, Unannealed, 100 mm Span)	144	°C	ISO 75-2/Be
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm)	136	°C	ASTM D648
Heat Deflection Temperature
1.8 MPa, Unannealed, 100 mm Span 11	136	°C	ISO 75-2/Ae
1.8 MPa, Unannealed, 64.0 mm Span 12	136	°C	ISO 75-2/Af
Heat Deflection Temperature 13 (1.8 MPa, Annealed)	142	°C	ISO 75-2/Ae
Vicat Softening Temperature	154	°C	ASTM D1525 14
Vicat Softening Temperature
--	141	°C	ISO 306/B50
--	143	°C	ISO 306/B120
Ball Pressure Test (125°C)	Pass		IEC 60695-10-2
CLTE - Flow (-40 to 40°C)	0.000047	cm/cm/°C	ASTM E831
CLTE - Flow (23 to 80°C)	0.00004	cm/cm/°C	ISO 11359-2
CLTE - Transverse (-40 to 40°C)	0.000085	cm/cm/°C	ASTM E831
CLTE - Transverse (-40 to 40°C)	0.000085	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.21	W/m/K	ISO 8302
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohm	IEC 60093
Volume Resistivity	> 1.0E+15	ohm·cm	IEC 60093
Relative Permittivity			IEC 60250
50 Hz	2.9
60 Hz	2.9
1 MHz	2.8
Dissipation Factor			IEC 60250
50 Hz	0.001
60 Hz	0.001
1 MHz	0.01
Comparative Tracking Index	150	V	IEC 60112
Electric Strength			IEC 60243-1
0.800 mm, in Oil	33	kV/mm
1.60 mm, in Oil	25	kV/mm
3.20 mm, in Oil	16	kV/mm
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
2.30 mm	V-0
1.80 mm	V-1
Glow Wire Flammability Index (1.00 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.00 mm)	825	°C	IEC 60695-2-13
Oxygen Index	36	%	ISO 4589-2
UL	Nominal Value	Unit	Test Method
RTI Str	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI Elec	130	°C	UL 746
Comparative Tracking Index (CTI) (PLC)	PLC 3		UL 746
Hot-wire Ignition (HWI) (PLC)	PLC 4		UL 746
High Amp Arc Ignition (HAI) (PLC)	PLC 4		UL 746
Outdoor Suitability	f2		UL 746C